PREPARATION OF MESO POROUS SILICA FROM BENTONITE BY ULTRAFINE GRINDING AND SELECTIVE LEACHING
DOI:
https://doi.org/10.30556/imj.Vol13.No1.2010.543Keywords:
meso porous silica, bentonite, ultrafine grinding, selective leachingAbstract
Preparation of meso porous silica from bentonite had been conducted by ultrafine grinding and leaching. The bentonite was taken from Nanggung, Bogor, West Java; it contains montmorillonite with porous struc- ture. The ultrafine grinding was carried out using planetary ball mill (PBM) in wet condition (wet milling) in methanol. Optimum milling time was reached in 30 hours and it produced 77.4 nm of particle size. The process was continued with selective leaching in sulphuric acid solution to increase the amount of SiO2 from 54.13% to 86.21%, which decreased Al2O3 and Fe2O3 content gradually from 23.09% and 7.33% to 4.96% and 0.89% respectively. The leaching process produced porous silica material with pore size 6.5 nm (meso porous); 278 m2/g of surface area and 0.75 mL/g of pore volume.
References
Arifin, M. dan Adjat Sudradjat, 1997. Bentonit : Bahan Galian Industri. Pusat Penelitian dan Pengembangan Mineral halaman 124-138.
Aziz, Muchtar, 2006. Pemanfaatan Mineral Al-Silikat untuk Bahan Katalis Hydrocarbon Cracking Minyak Bumi. Laporan Teknik Penelitian Pengolahan Mineral Puslitbang Teknologi Min- eral dan Batubara (tekMIRA).
Darmawan, Adi, 2004. Sintesis Katalis Mesopori Lempung Terpilar Sol Silika Berpengemban Ni dan Ti dari Lempung Alam Boyolali untuk Hidrorengkah Fraksi Berat Minyak Bumi Minas. Tesis, Fakultas MIPA Universitas Diponegoro.
Hinestroza, Juan P., 2009. Textiles Nanotechnology. http://nanotextiles.human.cornell.edu/.
Kresge, C.T., Leonowicz, M.E. and Roth, W.J., 1992. Ordered meso porous molecular sieves synthe- sized by a liquid–crystal template mechanism. Journal of Nature 359, 710–716.
Labaika, Ganjar, 2006. Kajian Terhadap Bentonit di Kabupaten Tasikmalaya dan Kemungkinannya Dijadikan Bahan Pembersih Minyak Sawit (CPO). Laporan Tehnik Penelitian Pusat Sumber Daya Geologi.
Okada, K, 2005. Preparation of porous silica from chlorite by selective acid leaching. Journal of Applied Bentonite Science 30, 116-124.
Rakhmatullah, 2007. Pembuatan Adsorben dari Zeolit Alam dengan Karakteristik Adsorption Properties untuk Kemurnian Bioetanol. Skripsi Program Studi Teknik Fisika, Institut Teknologi Bandung.
Rapp, Doreen, 2009. Nanostructured and Surface Charge of LDH. http://www.nanomineral.info/ DR_eng.htm.
Rees, Gregory, 2009. Developing wide line solid state NMR as a novel analytical approach to under- stand metals in catalytic technology for fuel cells and for therapeutic applications. http:// www2.warwick.ac.uk/fac/sci/physics/research/ condensedmatt/ nmr/members/postgraduates/ greg/.
Suquet, H., 1989. Effect of dry grinding and leaching on the crystal structure of chrysotile. Journal of Bentonites and Bentonite Minerals 37, 439–445.
Suryanarayana, C., 2001. Mechanical Alloying and Milling. Journal of Progress in Material Science.
Temuujin, J., 2001. Characterization of Porous Silica Prepared from Mechanically amorphized Kaolin- ite by Selective Leaching. Journal of Powder Technology 121, 259-262.
Temuujin, J., Kiyoshi Okada and K.J.D. MacKenzie, 2003. Preparation of Pororus Silica from Ver- miculite by Selective Leaching. Journal of Ap- plied Bentonite Science 2, 187-195.
Vogt, Ina, 2009. Magnetization of Microporous Agregates , http://www.nanomineral.info/ IV_eng.htm,.
Wati, Pratomo Budiman dan Sastrowardoyo, 2007. Difusi Cobalt dalam Na Bentonite dan Ca Ben- tonite. Jurnal Teknologi Pengelolaan Limbah, Pusat Teknologi Limbah Radioaktif.
Wijaya, Karna, 2009. Asam Padat Berbasis Montmorilonit sebagai Katalis dalam Proses Pembuatan Biodiesel dari Minyak Jelantah. Workshop advanced material, Fakultas MIPA Universitas Gajah Mada.
Zabukovec L N. and Kauèiè V., 2006. Review Article: Nanoporous Materials: From Catalysis and Hy- drogen Storage to Wastewater Treatment. Acta Chim. Slov.,53, 117–135.
Zamroni H., Thamzil Las, 2002. Pembuatan Pillared Lempung untuk Penyerapan Limbah Radio Aktif. Laporan Tehnik Penelitian P2LPR.
Downloads
Issue
Section
License
Indonesian Mining Journal provides immediate open access to its content on the principle that making research freely available to the public to supports a greater global exchange of knowledge.
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.